Application of 1B18 aerosolConformal Coating
- Allow 48 hours minimum to reach room temperature before using cans stored or received during cold weather.
- When applied in conditions of high ambient humidity, blushing (cloudy white film) may appear. Heating the coated assembly in an oven for 1/2 hour at 76°C eliminates this condition.
- Surface must be cleaned of dirt, wax, grease, flux residues and all similar contaminants for successful application of the coating.
- Mask areas not requiring coating from overspray using suitable non-silicone masking methods or materials.
- Shake can vigorously before using and repeat frequently during use.
- Best results are obtained by spraying from a distance of 30 – 40 cm in light even coats. A film thickness of 25 – 75 microns is sufficient to provide protection.
- To clean nozzle after use, hold can upside down, then press nozzle for a few seconds.
|
0.74 ± 0.02 g/cm³ |
- Solids Content, % by weight per Fed-Std-141, Meth. 4044
|
7 ± 1 % |
|
687.5 grams/liter |
- Drying Time to Handle per Fed-Std-141, Meth. 4061
|
30 minutes |
- Recommended Coating Thickness
|
25 -75 microns |
- Recommended Curing Conditions
|
24 hrs @ RT or 2 hrs @ 76°C |
- Time Required to Reach Optimum Properties
|
7 days |
|
HumiSeal® Stripper 1080, 1080A |
- Shelf Life at Room Temperature, DOM
|
24 months |
- Thermal Shock, 50 cycles per MIL-I-46058C
|
-65°C to 125°C |
- Coefficient of Thermal Expansion – TMA
|
67 ppm/°C |
- Glass Transition Temperature – DSC
|
42°C |
|
11.1 MPa |
|
V-0 |
- Dielectric Withstand Voltage, per MIL-I-46058C
|
>1500 volts |
- Dielectric Breakdown Voltage, per ASTM D149
|
6300 volts |
- Dielectric Constant, at 1MHz and 25°C, per ASTM D150-98
|
2.6 |
- Dissipation Factor, at 1MHz and 25°C, per ASTM D150-98
|
0.010 |
- Insulation Resistance, per MIL-I-46058C
|
5.5 x 1014 ohms (550TΩ) |
- Moisture Insulation Resistance, per MIL-I-46058C
|
7.0 x 1010 ohms (70GΩ) |
- Fungus Resistance, per ASTM G21
|
Passes |